New carbide solid Solution strengthening molybdenum alloy as follow:
Tungsten alloyed with molybdenum to improve the heat resistance strength study has been conducted in the past, based on the results, adding 25% W, the alloy to improve the melting point of about 200 ℃, so this series of great significance. Right (Mo-W)-Ti-Zr-C system more research can be considered, it is in the TZM or developed on the basis of TZC.
In 1989 at the International Pu Lanxi demonstrated Mo-W-Zr-Hf-C series alloys, can be considered, it is in the MHC and developed on the basis of ZHM. This series has the following composition alloy being vigorously Study:
M25WH1 | Mo23.72W1.20Hf-0.08C |
M25WH2 | Mo23.90W1.00Hf-0.06C |
M25WZH1 | Mo23.30W1.20Hf-0.40Zr-0.10C |
High-temperature strength of these alloys increases due W ZHM than HMC and strength of the alloy series, more than 20%, the alloy at between 950-1450 ℃ higher the amount of total carbon, high-temperature strength tends to decrease, plastic - brittle transition temperature trends on improving. At 950 ℃, the tensile fracture of these alloys exhibit ductile fracture, the bottom surface of the dimple can also see the kid 0.1 ~ 0.2μm of Hf and Zr oxide particles.
Se avete qualche interesse per la nostra lega di molibdeno o altri prodotti in lega di molibdeno, non esitate a contattarci via email: sales@chinatungsten.com,sales@xiamentungsten.com o per telefono: 86 592 512 9696.