Molibdênio Liga Cabeça Características

Head molybdenum alloy has the following characteristics:

Molybdenum alloy head temperature strength, high temperature, high hardness, coefficient of thermal expansion, elastic modulus, impact resistance but poor low temperature ductility, thus requiring greater than the head molybdenum alloy 700 ℃ conditions. To prevent high temperature oxidation and reduction drilling head table resistance to deformation, the surface of the head using the glass powder for anti-rust and surface lubrication.

Head carbon molybdenum alloy powder metallurgy

Density 9.3g/cm3;
HV temperature: 1600 ~ 20000MPa; 1100 ℃ HV: 480MPa;
Tensile strength: 354 ~ 450MPa, 1100 ℃ Tensile Strength: more than 200MPa; 1100 ℃: 3.0% ~ 3.5%.

TZM alloy casting 10.00g/cm3 head density, the hardness of the alloy, as shown in Table 1.

Table 1 TZM alloy hardness cast head.

Temperatura / ℃ Temperatura Ambiente 700 900 1100
Dureza / MPa >1970 >1250 >1200 >1150

Propriedades de tensão de curta duração de ligas: 1100> 189Mpa, 1100 ℃ mais de 10%, 1100 ℃ torsional Tb força> 176N.m, 1100 ℃ revoluções n = 3 voltas. Molibdênio liga cabeça usinagem densidade deformação> 10g/cm3, a dureza da liga, como mostrado na Tabela 2. 1200 ℃ resistência à tração de curto prazo> 330Mpa.

Tabela 2 molibdênio liga cabeça usinagem dureza deformação

Temperatura / ℃ Temperatura Ambiente 900
Dureza / MPa >2900 >1450

sales@chinatungsten.com,sales@xiamentungsten.com ou por telefone:: Se você tem algum interesse em nossa cabeça liga molibdênio ou outros produtos de liga de molibdênio, não hesite em contactar-nos por email, por favor 86 592 512 9696.

Address: 3F, No.25 WH Rd., Xiamen Software Park Ⅱ, FJ 361008,China
Phone:+86-592-5129696,+86-592-5129595;Fax:+86-592-5129797;Email:sales@chinatungsten.com,sales@xiamentungsten.com
Certified by MIIT:闽B2-20090025 闽ICP备06012101号-1
Copyright©1997 - 2016 ChinaTungsten Online All Rights Reserved