Moly Disilicide Coating - Dipping Sintering As Follows:

molybdenum disilicide1. The graphite grinding into 15mm * 15mm * 15mm * test block, the use of CSF-1A ultrasonic cleaner to surface cleaning and drying the reserve;

2. By a certain percentage of the Si powder, water and polyvinyl alcohol slurry preparation, grinding in a ball mill 1h;

3. Using dip coated in graphite blocks approximately 500μm thick slurry. Dried at 110 ℃ for 12h, and then in a vacuum oven at 1450 ℃ processing 2h, the graphite substrate can be prepared on the SiC coating gradient;

4. By a certain percentage weighing Mo and Si powders, using the same process as above was prepared Si-Mo slurry;

5. Using a dip coating method of the slurry Si-Mo coated on the inner layer of SiC, Si-Mo by controlling the number of the SiC slurry dip-coated on an inner layer of Si-Mo different thickness precoat slurry;

6. Dried at 110 ℃ 12h, and then in a vacuum oven at 1420 ℃ resistance calcined 2h.

Prepared by the molybdenum disilicide coating properties:

1) Si-MoSi2 outer layer of the coating prepared SiC/Si-MoSi2 oxidation performance is greatly affected. Si-MoSi2 outer layer thickness of about 80μm, the coating at 1400 ℃ showed good high temperature oxidation resistance. Too thin or too thick detrimental oxidation resistance.

2) coating the surface of the coating after oxidation to form a complete, dense layer of SiO2 glass to improve oxidation resistance of the material of the root causes of

If you have any interest in our moly disilicide coating or other molybdenum alloy products, please feel free to contact us by email: sales@chinatungsten.com,sales@xiamentungsten.com or by telephone:86 592 512 9696.

Address: 3F, No.25 WH Rd., Xiamen Software Park Ⅱ, FJ 361008,China
Phone:+86-592-5129696,+86-592-5129595;Fax:+86-592-5129797;Email:sales@chinatungsten.com,sales@xiamentungsten.com
Certified by MIIT:闽B2-20090025 闽ICP备06012101号-1
Copyright©1997 - 2016 ChinaTungsten Online All Rights Reserved