Molybdenum Alloy Anti-oxidation Coating Infiltration Prepared Method

Molybdenum alloy coating infiltration prepared method as follows:  

molybdenum disilicide1.Weight ratio according to the following ingredients and preparation of coatings.

Material powder: 100.
Containing silica: 40 ~ 90% of chromium powder: 5 ~ 30%, iron: 5 ~ 30%

Powders can also be made ​​according to the above ingredients and matching pre-alloy, and then ground to a powder.
Nitro varnish: 10 to 30 grams of ethyl acetate: 100 to 150 ml

2.In the 0.6 ~ 1atm under a spray pressure of the paint coating to the surface of the part.

3.Into the drying oven.

4.Then into the vacuum of 10-3 to 10-4 mm Hg temperature vacuum heat treatment furnace, furnace temperature should be controlled by the CCP near or above the melting point material powder. For 3 to 30 minutes.

5.Natural cooling in the furnace after completion of infiltration system.

If you have any interest in our molybdenum alloy coating or other molybdenum alloy products, please feel free to contact us by email: sales@chinatungsten.com,sales@xiamentungsten.com or by telephone:86 592 512 9696.

Address: 3F, No.25 WH Rd., Xiamen Software Park Ⅱ, FJ 361008,China
Phone:+86-592-5129696,+86-592-5129595;Fax:+86-592-5129797;Email:sales@chinatungsten.com,sales@xiamentungsten.com
Certified by MIIT:闽B2-20090025 闽ICP备06012101号-1
Copyright©1997 - 2016 ChinaTungsten Online All Rights Reserved